realloy classic
An universal CoCr bonding alloy compatible with all conventional ceramic materials
- The classicer
- Excellent bonding with ceramics
- Can be melted with using all known methods
- Easy finishing and easy to polish after casting
- Also suitable for laser welding
- Easy oxide removel after the ceramic firing
- Does not dust when milling
- Worldwide proven quality
- Biocompatible
Casting Ingot
Composition
Co 63,6 % | Cr 24,8 % | W 5,5 % | Mo 5,0 % | Si 1,1 % | Fe, Mn, Nb < 1%
This alloy is Nickel and Beryllium free and complies with EN ISO 22674, Typ 4
Proberties
Density 8,2 g/cm³
Vickers hardness 320 (HV10)
Linear CTE (25 - 500 °C) 14,3 (10-6·K-1)
Linear CTE (25 - 600 °C) 14,5 (10-6·K-1)
Melting interval 1360 - 1420 (°C)
Casting temperature 1500 (°C)
Recommended burning temperatur 980 (°C)
Proof strength (Rp 0,2) 460 (MPa)
Tensile strength (Rm) 760 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 12 (%)
Co 63,6 % | Cr 24,8 % | W 5,5 % | Mo 5,0 % | Si 1,1 % | Fe, Mn, Nb < 1%
This alloy is Nickel and Beryllium free and complies with EN ISO 22674, Typ 4
Proberties
Density 8,2 g/cm³
Vickers hardness 320 (HV10)
Linear CTE (25 - 500 °C) 14,3 (10-6·K-1)
Linear CTE (25 - 600 °C) 14,5 (10-6·K-1)
Melting interval 1360 - 1420 (°C)
Casting temperature 1500 (°C)
Recommended burning temperatur 980 (°C)
Proof strength (Rp 0,2) 460 (MPa)
Tensile strength (Rm) 760 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 12 (%)
Softblank
Powder 15-45 µm
Powder 10-30 µm